تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : IR spectra and dielectric properties of Cu-Ge ferrite IR spectra and dielectric properties of Cu-Ge ferrite   الموضوع : فيزياء  لغة الوثيقة : الانجليزية  المستخلص : The mixed ferrite Cu1+xGexFe2-2xO 4; where x = 0.0, 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3; was prepared from high purity oxides using the standard ceramic technique. The IR spectra were recorded on the range from 200 to 1000 cm-1. The two primary bands corresponding to tetrahedral νA and octahedral νB were observed around 575 cm-1 and 400 cm -1, respectively. It was found the threshold frequency νth for the electronic transition increases with increasing the Ge content. The Debye's temperature θD was calculated and it was found dependent on the type of charge carriers. AC conductivity σac with dielectric properties (dielectric constant ε′, dielectric loss ε″ and loss tangent tan δ) as a function of frequency (f = 102 → 106 Hz) at room temperature have been measured. The dispersion of the dielectric properties was discussed in the light of Koop's phenomenological theory. The phonon frequency νph which calculated from IR spectra for each composition of Cu-Ge ferrite was found to be higher than that calculated from the AC conductivity by a factor of about 104-105 Hz.  ردمد : 0254-0584  اسم الدورية : Materials Chemistry and Physics  المجلد : 130  العدد : 3  سنة النشر : 1432 هـ 2011 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Monday, April 9, 2012  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني Said A Mazen Mazen, Said A باحث دكتوراه dr.saidmazen@gmail.com علي محمد عبدالدايم Abdel Daiem, Ali Mohamed باحث دكتوراه abdeldaiem@hotmail.com الملفات اسم الملف النوع الوصف  32798.pdf pdf Abstract الرجوع إلى صفحة الأبحاث