تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : A novel strategy to synthesize cobalt hydroxide and Co3O 4 nanowires A novel strategy to synthesize cobalt hydroxide and Co3O 4 nanowires   الموضوع : فيزياء  لغة الوثيقة : الانجليزية  المستخلص : Cobalt hydroxide ultra fine nanowires were prepared by a facile hydrothermal route using hydrogen peroxide. This method provides a simple, low cost, and large-scale route to produce β-cobalt hydroxide nanowires with an average diameter of 5 nm and a length of ca. 10 μm, which show a predominant well-crystalline hexagonal brucite-like phase. Their thermal decomposition produced highly uniform nanowires of cobalt oxide (Co3O4) under temperature 500 °C in the presence of oxygen gas. The produced cobalt oxide was characterized by X-ray diffraction, transmission electronic microscopy, and selected-area electron diffraction. The results indicated that cobalt oxide nanowires with an average diameter of 10 nm and a length of ca. 600 nm have been formed, which show a predominant well-crystalline cubic face-centered like phase.  ردمد : 0022-3697  اسم الدورية : Journal of Physics and Chemistry of Solids  المجلد : 72  العدد : 7  سنة النشر : 1432 هـ 2011 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Wednesday, February 8, 2012  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني وليد السيد محمود Mahmoud, Waleed E باحث دكتوراه w_e_mahmoud@yahoo.com فيصل عبدالعزيز العقل Al-Agel, Faisal A باحث دكتوراه fagel@kau.edu.sa الملفات اسم الملف النوع الوصف  32226.pdf pdf Abstract الرجوع إلى صفحة الأبحاث