Electrical properties of thin films of a-GaxTe100-x composed of nanoparticles
Electrical properties of thin films of a-GaxTe100-x composed of nanoparticles
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : Thin films of GaxTe100-x (x = 3, 6, 9 and 12) have been synthesized by thermal evaporation. From SEM images, it is observed that all the films contain nanoparticles of sizes varying from 100 to 200 nm. The dc electrical conductivity of the as-deposited films of GaxTe 100-x nanoparticles is measured as a function of temperature range from 298 to 383 K, and increases exponentially with temperature. The value of the activation energy, calculated from the slope of ln σdc versus 1000/T plots, is found to decrease with increase in the Ga content. On the basis of the value of the pre-exponential factor σo, it is suggested that the conduction is due to thermally assisted tunneling of carriers in localized states near the band edges. The optical measurements suggest an indirect optical band gap in this system. The value of the optical band gap decreases on increasing the Ga concentration. 
ردمد : 0950-0839 
اسم الدورية : Philosophical Magazine Letters 
المجلد : 91 
العدد : 3 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, February 6, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
ذيشان حسين خانKhan, Zishan Hباحثدكتوراهzishan_hk@yahoo.co.in
شمشاد أحمد خانKhan, Shamshad Ahmedباحثدكتوراهshamshad_phys@yahoo.com
نعمان صلاحSalah, Numan باحثدكتوراهnsalah@kau.edu.sa
أحمد عبدالله الغامديAl-Ghamdi, Ahmad AباحثدكتوراهAGAMDI@kau.edu.sa
سامي سعيد حبيبHabib, Sami Saeedباحثدكتوراهshabib@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 32182.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث