Facile synthesis and optical properties of Co3O4 nanostructures by the microwave route
Facile synthesis and optical properties of Co3O4 nanostructures by the microwave route
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : Cobalt oxide (Co3O4) nanoplatelet shape like nanostructures have been successfully synthesized through a simple microwave route for the first time using cobalt acetate, NaOH and citric acid at 200 °C for 30 min. The structure and morphology of as-prepared Co 3O4 nanoplatelets are characterized by means of powder X-ray diffraction (XRD), Fourier transform infrared spectrum (FTIR), and scanning electron microscope (SEM). XRD measurements indicate that the product has a perfect crystalline cubic phase of Co3O4 with a lattice constant a=8.082 Å. The SEM images show that the obtained Co 3O4 nanopowder consists of nanoplatelets with diameter 125 nm and thickness 20 nm. Energy-dispersive X-ray spectroscopy (EDS) show that the composition of Co3O4 is stoichiometric. Room temperature photoluminescence measurement is exhibited by a strong UV emission and a suppressed green emission, confirming the good optical properties for the as-prepared Co3O4 nanoplatelets. 
ردمد : 0749-6036 
اسم الدورية : Superlattices and Microstructures 
المجلد : 49 
العدد : 4 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, February 5, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
ريم محمد الطويرقيAl-Tuwirqi, Reem Mباحثدكتوراهraltuwirqi@kau.edu.sa
أحمد عبدالله الغامديAl-Ghamdi, Ahmad AباحثدكتوراهAGAMDI@kau.edu.sa
Nadia Abdel AalAbdel Aal, Nadia باحثدكتوراه 
Ahmad Ali UmarUmar, Ahmad Aliباحثدكتوراه 
وليد السيد محمودMahmoud, Waleed Eباحثدكتوراهw_e_mahmoud@yahoo.com

الملفات

اسم الملفالنوعالوصف
 32171.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث