Electrodeposition and morphology analysis of nickel nanoparticles from sulphate bath
Electrodeposition and morphology analysis of nickel nanoparticles from sulphate bath
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : The electrodeposition of Nickel in the presence of organic compound was studied systematically as function of the nature of the organic additive. The effects of various parameters such as nickel sulphate concentration, bath temperature, current density have been investigated on deposit physical appearance. The tolerance limits and the effect of combined organic additive have been identified under different experimental conditions. We have used scanning electron microscopy (SEM) to characterize the surface morphology of deposits. The SEM pictures show the formation of domain growth of nickel in which nanoparticles are mostly concentrated at domain boundaries and incorporated in the coating matrix to improve the surface mechanical properties. The coatings are found to be highly adherent and uniform by adding calixarene derivative as organic additive at very low concentration. Threedimensional AFM images confirm that the presence of calixarene derivative improves the surface smoothness. The microhardness measurements were performed and the structure of deposits was examined by X-ray diffraction. 
ردمد : 1348-0391 
اسم الدورية : e-Journal of Surface Science and Nanotechnology 
المجلد : 8 
العدد : 2010 
سنة النشر : 1431 هـ
2010 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, November 16, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
Kamel BelhamelBelhamel, Kamel باحثدكتوراهkbelhamel@yahoo.fr
Hamid KherazKheraz, Hamid باحثدكتوراه 
Rainer LudwigLudwig, Rainer باحثدكتوراه 
T. K Dzung NguenNguen, T. K Dzungباحثدكتوراه 
Nicholas AllsopAllsop, Nicholas باحثدكتوراه 
صالح سالم الجعيدAl-Juaid, Salih Sباحثدكتوراهsaljuaid@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 31257.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث